GB 80 Ferrotungsten Block Special Steel for Smelting 75-80%Few

• Customization: Available
• Product Type: Lump
• Material: FeW
• Model NO.: few-0001
• Carbon Content: Low Carbon
• Products Name: Ferrotungsten
• Color: Gray
• Min. Order: 100kg
• HS: 7202801000
• Transport Package: 100kg Drum Packing
• Specification: ferrotungsten 70 75 80
• Trademark: XINPAI
• Origin: Qingdao China
• HS Code: 7202801000
• Production Capacity: 1000ton/Year
• Package Size: 10.00cm * 30.00cm * 30.00cm
• Package Gross Weight: 10.000kg

Product Description

Product Description

 

Ferrotungsten block

Product introduction:
Ferrotungsten powder has better fluidity than Ferrotungsten block, and is widely used in the production of welding rods and flux-cored wires.
Ferrotungsten smelting ferrotungsten is an alloy of tungsten and iron. It is used as an alloy additive of tungsten element in steelmaking and casting. Ferrotungsten is one of the most important alloy elements in the production of special steel, and is widely used in the production of high-speed tool steel, alloy structural steel, magnetic steel, heat-resistant steel and stainless steel. Tungsten in steel can combine with other elements to form complex carbides, which can refine the grain of steel, thus improving the red hardness, wear resistance and impact strength of steel. It can not only reduce the elongation of steel to a small extent, but also improve the strength limit and yield point of steel, as well as the hardness and wear resistance of steel.
Production process:
The agglomeration method adopts an open electric furnace that can move on the track and the upper section of the furnace body can be disassembled, using carbon as the reducing agent. The mixed furnace charge composed of refined tungsten ore, asphalt coke (or petroleum coke) and slag making agent (bauxite) is added to the furnace in batches. The metal refined in the furnace is generally viscous. With the increase of thickness, the lower part gradually solidifies. Stop the furnace when the furnace is full, pull out the furnace body, and remove the upper furnace body to condense the agglomeration. Then take out the clot for crushing and finishing; Pick out the edge, slag and unqualified parts for remelting.
 

NO.1		Impurity content is not more than (%)
		C	P	S	Si	Mn	Cu	As	Bi	Pb	Sb	Sn
FeW80-A	75-85	0.10	0.03	0.06	0.5	0.25	0.10	0.06	0.05	0.05	0.05	0.06
FeW80-B	75-85	0.30	0.04	0.07	0.7	0.35	0.12	0.08	-	-	0.05	0.08
FeW80-C	75-85	0.40	0.05	0.08	0.7	0.50	0.15	0.10	-W	-	0.05	0.08
FeW70	≥70	0.80	0.06	0.10	1.0	0.60	0.18	0.10	-	-	0.05	0.10